HIP
I3 HIP Furnace
I3CC20 hot isostatic pressing configuration with C/C or molybdenum heating.
The published I3CC20 configuration lists a 350 mm diameter by 700 mm work zone, 100 / 150 / 200 MPa gas pressure, and C/C heating to 2000°C, with a molybdenum-heated version to 1400°C. Temperature and pressure limits are configuration dependent and must be confirmed together for the intended process.
Key Features
Technical Highlights
Simultaneous heat and isostatic argon gas pressure to close internal porosity
Accepts as-cast or sintered parts and sealed, outgassed powder capsules
Controlled cooling and depressurization sequence before unloading
Pressure, temperature and work zone confirmed together for the intended process
Process Flow
HIP Process Overview
Hot isostatic pressing uses simultaneous heat and isostatic gas pressure to eliminate internal porosity and achieve near-full density.
Lifecycle support
Plan support alongside the equipment configuration.
Organize equipment records, technical questions, operating procedures, and handover materials around the project scope.
Selection guide
Confirm the process window before quotation.
For faster engineering review, prepare the core process boundaries before sending an inquiry.
Can the chamber be customized?
Yes. Chamber size, heating zone, fixture, pressure, and atmosphere configuration should be confirmed through technical review.
Is a process test recommended?
For new materials or demanding density targets, a sample process discussion helps reduce equipment selection risk.
What should be sent with an inquiry?
Material, target temperature, pressure or load, atmosphere, workpiece size, and expected capacity are the most useful inputs.
Which certifications and delivery dates apply?
Share the destination country, required standards and installation date. Applicable declarations, certificates, acceptance scope and delivery schedule are confirmed for the quoted configuration; they are not universal catalogue guarantees.
Official Specification Tables
Imported from Haoyue's official product data and reorganized for clearer technical review.
| Product number | Furnace size (mm) | Gas pressure (MPa) | Heating material | Heating power (kw) | Vacuum degree(Pa) | Max. temperature (°C) |
|---|---|---|---|---|---|---|
| I3CC20 | Φ 350x700 | 100/150/200 | C/C | 200 | 10 | 2000 |
| 13MO14 | Φ 350x700 | 100/150/200 | MO | 200 | 10 | 1400 |
Typical Applications
Related products
Review similar furnace options.
Gas Pressure
G2 Pressure Sintering Furnace
Integrates positive pressure dewaxing, vacuum dewaxing, vacuum sintering, partial pressure sintering, pressure sintering, atmosphere control, and cooling for high-pressure nitrogen or argon sintering.
HIP
I1 HIP Furnace
The published I1CC20 configuration lists a 100 mm diameter by 150 mm work zone, 200 MPa gas pressure, and C/C heating to 2000°C, with a molybdenum-heated version to 1400°C. Temperature and pressure limits are configuration dependent and must be confirmed together for the intended process.
HIP
I2 HIP Furnace
The I2 is an I Series hot isostatic pressing furnace. HIP applies heat and isostatic gas pressure at the same time to reduce internal porosity in castings, sintered parts and powder capsules. Temperature, pressure and work zone are confirmed together for the intended process.
Gallery And Media
Review product images, equipment details, and available media before sending a technical inquiry.
Technical Downloads
Use these documents to prepare a technical proposal request with material, atmosphere, temperature, pressure, and chamber details.
HIP Furnace Requirement Sheet
Technical intake sheet for hot isostatic pressing projects, including material, pressure, chamber size, and batch expectations.
Request Technical Proposal